Today TPU/ABS is mostly used in the automotive industry, as a material for thermoforming of interior parts of cars, buses, tractors and external trunks. Thanks to its mechanical strength, it is used for the manufacture of suitcases, trays for transportation, trays for RAIL and air transport, finishing and facing work; with its help it is easy to revet all surfaces, including facades of residential and industrial buildings. Excellent and durable advertisement and information stands are made of this plastic sheets, as well as showcases, dividers in public buildings.

CHEMICAL RESISTANCE

good weather resistance, high resistance to oils, fats, greases and various solvents

PHYSICAL PROPERTIES

resistant to temperature change, extremely resistant to atmospheric conditions

OPERATING TEMPERATURE

the maximum permanent operating temperature: 75-85°C

PROCESSING

• stamping
• pneumatic vacuum forming
• machining
• welding
• bonding

• This plastic sheet is well resistant to abrasion and scratching
• It has got anti-slip properties and properties of noise reduction
• It is pleasant to touch, its surface is called Soft Touch (thanks to TPU)
• It has good strength and ductility at low temperatures
• It has got excellent chemical resistance when contacting with oils, hydrocarbons and many solvents (better than ABS)
• It is also resistant to hydrolysis and contact with microorganisms (bacteria, fungi, etc.)
• Its deformation under load is minor because it is high resistant to compression
• High resistance of cut material to further break
• The possibility of making sheet’s surface with varying degrees of gloss/mattness
• The opportunity to manufacture the plates with antistatic surface (resistance to 105 Ω)
• The possibility of extrusion with recycled ABS

• Density, no less than -
  UNIT - g/cm³
  TEST METHOD, ISO - 1183
  VALUES - 1.06


• Yield stress -
  UNIT -Mpa
  TEST METHOD, ISO - 527
  VALUES - 28


• Тensile strength at break, no less than - 5
  UNIT - %
  TEST METHOD, ISO - 527
  VALUES - 10


• Charpy unnotched impact strength - 23°C
  UNIT - kJ/m²
  TEST METHOD, ISO - 179
  VALUES -


• Charpy unnotched impact strength - -20°C
  UNIT - kJ/m²
  TEST METHOD, ISO - 179
  VALUES -


• Abrasion resistance - On the sample d 100 mm abrasive wheel is W18 holddown pressure is 500 g
  UNIT - g
  TEST METHOD, ISO -
  VALUES - 0.05


• Flexural Modulus, no less -
  UNIT - Mpa
  UTEST METHOD, ISO - 178
  VALUES - 2200-2300


• Vicat softening temperature - 50H/50°C
  UNIT - °С
  TEST METHOD, ISO - 306/B120
  VALUES - 98


• Heat deflection temperature, (НDT), no less than - 1.8 MPa.
  UNIT - °С
  TEST METHOD, ISO - 75-2Ae
  VALUES - 95

1.5 mm to 10 mm Width Maximum 1 mtr, Extruded.

• Standard White
  Black
  Grey

UV Stabilised, Fire Retardent, High Impact, High Gloss & Low Gloss.